# CITATION: Erhart, Juslin, Goy, Nordlund, Müller, Albe, J. Phys.: Condens. Mat. 18, 6585 (2006) O O O 1 0.82595 0.0 0.035608 0.046496 -0.45056 1 1 2.7732859784544366 527.6505089731846 2.45 0.2 3.8448836805292306 1388.081581389159 O O Zn 1 0.019335 0.0 0.014108 0.084028 -0.30545 0 0 0 0 2.60 0.20 0 0 O Zn O 1 0.82595 0.0 0.035608 0.046496 -0.45056 0 0 0 0 2.45 0.2 0 0 O Zn Zn 1 0.019335 0.0 0.014108 0.084028 -0.30545 1 1 2.513642455305317 6304.327815151947 2.60 0.20 2.628013187021709 7344.239422800065 Zn O O 1 0.019335 0.0 0.014108 0.084028 -0.30545 1 1 2.513642455305317 6304.327815151947 2.60 0.20 2.628013187021709 7344.239422800065 Zn O Zn 1 4.3909e-5 0.0 77.916 0.91344 -1.0 0 0 0 0 2.85 0.20 0 0 Zn Zn O 1 0.019335 0.0 0.014108 0.084028 -0.30545 0 0 0 0 2.60 0.20 0 0 Zn Zn Zn 1 4.3909e-5 0.0 77.916 0.91344 -1.0 1 1 1.7965160854189726 115.1593431985539 2.85 0.20 3.261395301469603 2258.730853636288