# DATE: 2017-05-16 CONTRIBUTOR: Laurent Pizzagalli CITATION: G. Lucas, M. Bertolus, and L. Pizzagalli, J. Phys. : Condens. Matter 22, 035802 (2010) # # element 1, element 2, element 3, # A B cutoffA cutoffC alpha beta eta # gamma lambda mu rho sigma Q0 # u1 u2 u3 u4 # # units for each parameters: # A , lambda are in eV # B, cutoffA, cutoffC, gamma, sigma are in Angstrom # alpha, beta, eta, mu, rho, Q0, u1-u4 are pure numbers # Si Si Si 5.488043 1.446435 2.941586 2.540193 3.066580 0.008593 0.589390 1.135256 2.417497 0.629131 1.343679 0.298443 208.924548 -0.165799 32.557 0.286198 0.66 C C C 10.222599 0.959814 2.212263 1.741598 1.962090 0.025661 0.275605 1.084183 3.633621 0.594236 2.827634 0.536561 289.305617 -0.165799 32.557 0.286198 0.66 C Si Si 7.535967 1.177019 2.534972 1.973974 2.507738 0.015347 0.432497 1.191567 3.025559 0.611684 2.061835 0.423863 249.115082 -0.165799 32.557000 0.286198 0.660000 Si C C 7.535967 1.177019 2.534972 1.973974 2.507738 0.015347 0.432497 1.191567 3.025559 0.611684 2.061835 0.423863 249.115082 -0.165799 32.557000 0.286198 0.660000 Si Si C 5.488043 1.446435 2.941586 2.540193 3.066580 0.008593 0.510944 1.135256 2.721528 0.620407 1.343679 0.298443 229.019815 -0.165799 32.557000 0.286198 0.660000 Si C Si 7.535967 1.177019 2.534972 1.973974 2.507738 0.015347 0.510944 1.191567 2.721528 0.620407 2.061835 0.423863 229.019815 -0.165799 32.557000 0.286198 0.660000 C C Si 10.222599 0.959814 2.212263 1.741598 1.962090 0.025661 0.354051 1.084183 3.329590 0.602960 2.827634 0.536561 269.210350 -0.165799 32.557000 0.286198 0.660000 C Si C 7.535967 1.177019 2.534972 1.973974 2.507738 0.015347 0.354051 1.191567 3.329590 0.602960 2.061835 0.423863 269.210350 -0.165799 32.557000 0.286198 0.660000