    "property-id" "tag:staff@noreply.openkim.org,2014-04-15:property/structure-tetragonal-crystal-npt"
    "instance-id" 1
    "space-group" {
        "source-value" "P4_2nm"
    }
    "basis-atom-coordinates" {
        "source-value" [
            [
                0
                0
                0.347958
            ]
            [
                0.5
                0.5
                0.847958
            ]
            [
                0
                0
                0.996309
            ]
            [
                0.5
                0.5
                0.496309
            ]
            [
                0.177069
                0.822931
                0.148911
            ]
            [
                0.196699
                0.803301
                0.858543
            ]
            [
                0.234766
                0.765234
                0.487977
            ]
            [
                0.265234
                0.265234
                0.987977
            ]
            [
                0.303301
                0.303301
                0.358543
            ]
            [
                0.322931
                0.322931
                0.648911
            ]
            [
                0.696699
                0.696699
                0.358543
            ]
            [
                0.677069
                0.677069
                0.648911
            ]
            [
                0.734766
                0.734766
                0.987977
            ]
            [
                0.765234
                0.234766
                0.487977
            ]
            [
                0.822931
                0.177069
                0.148911
            ]
            [
                0.803301
                0.196699
                0.858543
            ]
        ]
    }
    "species" {
        "source-value" [
            "Li"
            "Li"
            "V"
            "V"
            "F"
            "F"
            "F"
            "F"
            "F"
            "F"
            "F"
            "F"
            "F"
            "F"
            "F"
            "F"
        ]
    }
    "cauchy-stress" {
        "source-value" [
            0
            0
            0
            0
            0
            0
        ]
        "source-unit" "GPa"
    }
    "temperature" {
        "source-value" 0
        "source-unit" "K"
    }
    "a" {
        "source-value" 4.84811708
        "source-unit" "angstrom"
    }
    "c" {
        "source-value" 8.84417165
        "source-unit" "angstrom"
    }
}