Reactive MD-force field: Water/Ca-OH 11.9.11 39 ! Number of general parameters 50.0000 !Overcoordination parameter 9.5469 !Overcoordination parameter 26.5405 !Valency angle conjugation parameter 1.7224 !Triple bond stabilisation parameter 6.8702 !Triple bond stabilisation parameter 60.4850 !C2-correction 1.0588 !Undercoordination parameter 4.6000 !Triple bond stabilisation parameter 12.1176 !Undercoordination parameter 13.3056 !Undercoordination parameter -70.5044 !Triple bond stabilization energy 0.0000 !Lower Taper-radius 10.0000 !Upper Taper-radius 2.8793 !Not used 33.8667 !Valency undercoordination 6.0891 !Valency angle/lone pair parameter 1.0563 !Valency angle 2.0384 !Valency angle parameter 6.1431 !Not used 6.9290 !Double bond/angle parameter 0.3989 !Double bond/angle parameter: overcoord 3.9954 !Double bond/angle parameter: overcoord -2.4837 !Not used 5.7796 !Torsion/BO parameter 10.0000 !Torsion overcoordination 1.9487 !Torsion overcoordination -1.2327 !Conjugation 0 (not used) 2.1645 !Conjugation 1.5591 !vdWaals shielding 0.1000 !Cutoff for bond order (*100) 2.1365 !Valency angle conjugation parameter 0.6991 !Overcoordination parameter 50.0000 !Overcoordination parameter 1.8512 !Valency/lone pair parameter 0.5000 !Not used 20.0000 !Not used 5.0000 !Molecular energy (not used) 0.0000 !Molecular energy (not used) 2.6962 !Valency angle conjugation parameter 6 ! Nr of atoms; cov.r; valency;a.m;Rvdw;Evdw;gammaEEM;cov.r2;# alfa;gammavdW;valency;Eunder;Eover;chiEEM;etaEEM;n.u. cov r3;Elp;Heat inc.;n.u.;n.u.;n.u.;n.u. ov/un;val1;n.u.;val3,vval4 C 1.3817 4.0000 12.0000 1.8903 0.1838 0.9000 1.1341 4.0000 9.7559 2.1346 4.0000 34.9350 79.5548 5.9666 7.0000 0.0000 1.2114 0.0000 202.5551 8.9539 34.9289 13.5366 0.8563 0.0000 -2.8983 2.5000 1.0564 4.0000 2.9663 0.0000 0.0000 0.0000 H 0.8930 1.0000 1.0080 1.3550 0.0930 0.8203 -0.1000 1.0000 8.2230 33.2894 1.0000 0.0000 121.1250 3.7248 9.6093 1.0000 -0.1000 0.0000 61.6606 3.0408 2.4197 0.0003 1.0698 0.0000 -19.4571 4.2733 1.0338 1.0000 2.8793 0.0000 0.0000 0.0000 O 1.2450 2.0000 15.9990 2.3890 0.1000 1.0898 1.0548 6.0000 9.7300 13.8449 4.0000 37.5000 116.0768 8.5000 8.3122 2.0000 0.9049 0.4056 59.0626 3.5027 0.7640 0.0021 0.9745 0.0000 -3.5500 2.9000 1.0493 4.0000 2.9225 0.0000 0.0000 0.0000 Ca 1.9076 2.0000 40.0870 2.7037 0.2027 1.0000 1.0000 2.0000 10.5471 27.5993 3.0000 38.0000 0.0000 -2.5000 6.5000 0.0000 -1.3000 0.0000 220.0000 49.9248 0.3370 0.0000 0.0000 0.0000 -4.4049 4.0000 1.0564 8.0000 2.9663 0.0000 0.0000 0.0000 Si 2.1932 4.0000 28.0600 1.8951 0.1737 0.5947 1.2962 4.0000 11.3429 5.2054 4.0000 21.7115 139.9309 4.2033 5.5558 0.0000 -1.0000 0.0000 128.2031 9.0751 23.8188 0.8381 0.8563 0.0000 -4.1684 2.0754 1.0338 4.0000 2.5791 1.4000 0.2000 13.0000 X -0.1000 2.0000 1.0080 2.0000 0.0000 1.0000 -0.1000 6.0000 10.0000 2.5000 4.0000 0.0000 0.0000 8.5000 1.5000 0.0000 -0.1000 0.0000 -2.3700 8.7410 13.3640 0.6690 0.9745 0.0000 -11.0000 2.7466 1.0338 2.0000 2.8793 0.0000 0.0000 0.0000 13 ! Nr of bonds; Edis1;LPpen;n.u.;pbe1;pbo5;13corr;pbo6 pbe2;pbo3;pbo4;n.u.;pbo1;pbo2;ovcorr 1 1 158.2004 99.1897 78.0000 -0.7738 -0.4550 1.0000 37.6117 0.4147 0.4590 -0.1000 9.1628 1.0000 -0.0777 6.7268 1.0000 0.0000 1 2 169.4760 0.0000 0.0000 -0.6083 0.0000 1.0000 6.0000 0.7652 5.2290 1.0000 0.0000 1.0000 -0.0500 6.9136 0.0000 0.0000 2 2 153.3934 0.0000 0.0000 -0.4600 0.0000 1.0000 6.0000 0.7300 6.2500 1.0000 0.0000 1.0000 -0.0790 6.0552 0.0000 0.0000 1 3 158.6946 107.4583 23.3136 -0.4240 -0.1743 1.0000 10.8209 1.0000 0.5322 -0.3113 7.0000 1.0000 -0.1447 5.2450 0.0000 0.0000 3 3 142.2858 145.0000 50.8293 0.2506 -0.1000 1.0000 29.7503 0.6051 0.3451 -0.1055 9.0000 1.0000 -0.1225 5.5000 1.0000 0.0000 2 3 160.0000 0.0000 0.0000 -0.5725 0.0000 1.0000 6.0000 0.5626 1.1150 1.0000 0.0000 1.0000 -0.0920 4.2790 0.0000 0.0000 2 4 0.0000 0.0000 0.0000 -0.0203 -0.1418 1.0000 13.1260 0.0230 8.2136 -0.1310 0.0000 1.0000 -0.2692 6.4254 0.0000 24.4461 3 4 65.2822 0.0000 43.3991 0.5314 -0.3000 1.0000 36.0000 0.0025 0.6946 -0.2500 12.0000 1.0000 -0.0404 9.3919 1.0000 24.4461 4 4 87.4241 0.0000 0.0000 -0.1526 -0.2000 0.0000 16.0000 0.4154 0.2550 -0.2000 10.0000 1.0000 -0.0841 4.1567 0.0000 0.0000 2 5 250.0000 0.0000 0.0000 -0.7128 0.0000 1.0000 6.0000 0.1186 18.5790 1.0000 0.0000 1.0000 -0.0731 7.4983 0.0000 0.0000 3 5 274.8339 5.0000 0.0000 -0.5884 -0.3000 1.0000 36.0000 0.2131 9.9772 -0.2572 28.8153 1.0000 -0.1130 8.4790 6.0658 0.0000 4 5 0.0000 0.0000 0.0000 0.5000 -0.3000 1.0000 16.0000 0.5000 0.5000 -0.2500 15.0000 1.0000 -0.1000 9.0000 0.0000 0.0000 5 5 70.9120 54.0531 30.0000 0.4931 -0.3000 1.0000 16.0000 0.0392 0.2476 -0.8055 7.1248 1.0000 -0.1009 8.7229 0.0000 0.0000 8 ! Nr of off-diagonal terms; Ediss;Ro;gamma;rsigma;rpi;rpi2 1 2 0.1239 1.4004 9.8467 1.1210 -1.0000 -1.0000 2 3 0.0283 1.2885 10.9190 0.9215 -1.0000 -1.0000 1 3 0.1156 1.8520 9.8317 1.2854 1.1352 1.0706 2 4 0.0100 1.6000 13.2979 -1.0000 -1.0000 -1.0000 3 4 0.1246 1.7500 12.3414 1.8680 -1.0000 -1.0000 2 5 0.2000 1.5207 12.9535 1.2125 -1.0000 -1.0000 3 5 0.1836 1.9157 10.9070 1.7073 1.2375 -1.0000 4 5 0.1000 1.9000 11.0000 -1.0000 -1.0000 -1.0000 34 ! Nr of angles;at1;at2;at3;Thetao,o;ka;kb;pv1;pv2 1 1 1 59.0573 30.7029 0.7606 0.0000 0.7180 6.2933 1.1244 1 1 2 65.7758 14.5234 6.2481 0.0000 0.5665 0.0000 1.6255 2 1 2 70.2607 25.2202 3.7312 0.0000 0.0050 0.0000 2.7500 1 2 2 0.0000 0.0000 6.0000 0.0000 0.0000 0.0000 1.0400 1 2 1 0.0000 3.4110 7.7350 0.0000 0.0000 0.0000 1.0400 2 2 2 0.0000 27.9213 5.8635 0.0000 0.0000 0.0000 1.0400 1 1 3 49.6811 7.1713 4.3889 0.0000 0.7171 10.2661 1.0463 3 1 3 77.7473 40.1718 2.9802 -25.3063 1.6170 -46.1315 2.2503 2 1 3 65.0000 13.8815 5.0583 0.0000 0.4985 0.0000 1.4900 1 3 1 73.5312 44.7275 0.7354 0.0000 3.0000 0.0000 1.0684 1 3 3 79.4761 36.3701 1.8943 0.0000 0.7351 67.6777 3.0000 3 3 3 80.7324 30.4554 0.9953 0.0000 1.6310 50.0000 1.0783 1 3 2 70.1880 20.9562 0.3864 0.0000 0.0050 0.0000 1.6924 2 3 3 75.6935 50.0000 2.0000 0.0000 1.0000 0.0000 1.1680 2 3 2 85.8000 9.8453 2.2720 0.0000 2.8635 0.0000 1.5800 1 2 3 0.0000 25.0000 3.0000 0.0000 1.0000 0.0000 1.0400 3 2 3 0.0000 15.0000 2.8900 0.0000 0.0000 0.0000 2.8774 2 2 3 0.0000 8.5744 3.0000 0.0000 0.0000 0.0000 1.0421 3 4 3 4.3550 6.7261 3.5630 0.0000 0.4097 0.0000 1.4173 4 3 4 2.1633 7.8692 12.0000 0.0000 1.2016 0.0000 2.3080 2 3 4 79.4055 2.5449 3.4541 0.0000 0.8181 0.0000 1.0000 3 3 4 70.0000 25.0000 1.0000 0.0000 1.0000 0.0000 1.2500 5 5 5 78.5339 36.4328 1.0067 0.0000 0.1694 0.0000 1.6608 2 5 5 77.2616 5.0190 7.8944 0.0000 4.0000 0.0000 1.0400 2 5 2 75.7983 14.4132 2.8640 0.0000 4.0000 0.0000 1.0400 3 5 5 86.3294 18.3879 5.8529 0.0000 1.7361 0.0000 1.2310 2 5 3 73.6998 40.0000 1.8782 0.0000 4.0000 0.0000 1.1290 3 5 3 79.5581 34.9140 1.0801 0.0000 0.1632 0.0000 2.2206 5 3 5 82.3364 4.7350 1.3544 0.0000 1.4627 0.0000 1.0400 2 3 5 90.0000 6.6857 1.6689 0.0000 2.5771 0.0000 1.0400 3 3 5 92.1207 24.3937 0.5000 0.0000 1.7208 0.0000 3.0000 2 2 5 0.0000 47.1300 6.0000 0.0000 1.6371 0.0000 1.0400 5 2 5 0.0000 27.4206 6.0000 0.0000 1.6371 0.0000 1.0400 3 2 5 0.0000 5.0000 1.0000 0.0000 1.0000 0.0000 1.2500 26 ! Nr of torsions;at1;at2;at3;at4;;V1;V2;V3;V2(BO);vconj;n.u;n 1 1 1 1 -0.2500 34.7453 0.0288 -6.3507 -1.6000 0.0000 0.0000 1 1 1 2 -0.2500 29.2131 0.2945 -4.9581 -2.1802 0.0000 0.0000 2 1 1 2 -0.2500 31.2081 0.4539 -4.8923 -2.2677 0.0000 0.0000 1 1 1 3 -0.3495 22.2142 -0.2959 -2.5000 -1.9066 0.0000 0.0000 2 1 1 3 0.0646 24.3195 0.6259 -3.9603 -1.0000 0.0000 0.0000 3 1 1 3 -0.5456 5.5756 0.8433 -5.1924 -1.0180 0.0000 0.0000 1 1 3 1 1.7555 27.9267 0.0072 -2.6533 -1.0000 0.0000 0.0000 1 1 3 2 -1.4358 36.7830 -1.0000 -8.1821 -1.0000 0.0000 0.0000 2 1 3 1 -1.3959 34.5053 0.7200 -2.5714 -2.1641 0.0000 0.0000 2 1 3 2 -2.5000 70.0597 1.0000 -3.5539 -2.9929 0.0000 0.0000 1 1 3 3 0.6852 11.2819 -0.4784 -2.5000 -2.1085 0.0000 0.0000 2 1 3 3 0.1933 80.0000 1.0000 -4.0590 -3.0000 0.0000 0.0000 3 1 3 1 -1.9889 76.4820 -0.1796 -3.8301 -3.0000 0.0000 0.0000 3 1 3 2 0.2160 72.7707 -0.7087 -4.2100 -3.0000 0.0000 0.0000 3 1 3 3 -2.5000 71.0772 0.2542 -3.1631 -3.0000 0.0000 0.0000 1 3 3 1 2.5000 -0.6002 1.0000 -3.4297 -2.8858 0.0000 0.0000 1 3 3 2 -2.5000 -3.3822 0.7004 -5.4467 -2.9586 0.0000 0.0000 2 3 3 2 2.5000 -4.0000 0.9000 -2.5000 -1.0000 0.0000 0.0000 1 3 3 3 1.2329 -4.0000 1.0000 -2.5000 -1.7479 0.0000 0.0000 2 3 3 3 0.8302 -4.0000 -0.7763 -2.5000 -1.0000 0.0000 0.0000 3 3 3 3 -2.5000 -4.0000 1.0000 -2.5000 -1.0000 0.0000 0.0000 0 1 2 0 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0 2 2 0 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0 2 3 0 0.0000 0.1000 0.0200 -2.5415 0.0000 0.0000 0.0000 0 1 1 0 0.0000 50.0000 0.3000 -4.0000 -2.0000 0.0000 0.0000 0 3 3 0 0.5511 25.4150 1.1330 -5.1903 -1.0000 0.0000 0.0000 1 ! Nr of hydrogen bonds;at1;at2;at3;Rhb;Dehb;vhb1 3 2 3 2.1200 -3.5800 1.4500 19.5000