element(s):
['Ni', 'Ti']
AFLOW prototype label:
AB_oC8_63_c_c
Parameter names:
['a', 'b/a', 'c/a', 'y1', 'y2']
model type (only 'standard' supported at this time):
standard
number of parameter sets:
1
Parameter values for parameter set 0:
['3.0244', '3.1394987', '1.3058127', '0.91444432', '0.64244755']
model name:
MEAM_LAMMPS_KoGrabowskiNeugebauer_2015_NiTi__MO_663355627503_002
==== Building ASE atoms object with: ====
representative atom symbols =  ['Ni', 'Ti']
representative atom coordinates =  [[0.         0.91444432 0.25      ]
 [0.         0.64244755 0.25      ]]
spacegroup =  63
cell =  [[3.0244, 0, 0], [0, 9.4951, 0], [0, 0, 3.9493]]
=========================================
      Step     Time          Energy          fmax
BFGS:    0 21:47:59      -40.251286         1.071013
BFGS:    1 21:48:00      -40.322988         0.965054
BFGS:    2 21:48:00      -40.514239         0.591297
BFGS:    3 21:48:00      -40.628598         0.328828
BFGS:    4 21:48:00      -40.658566         0.250454
BFGS:    5 21:48:00      -40.664584         0.230339
BFGS:    6 21:48:00      -40.680853         0.220353
BFGS:    7 21:48:00      -40.682111         0.214951
BFGS:    8 21:48:00      -40.693682         0.154946
BFGS:    9 21:48:01      -40.703536         0.133462
BFGS:   10 21:48:01      -40.711786         0.147818
BFGS:   11 21:48:01      -40.718006         0.163368
BFGS:   12 21:48:01      -40.721784         0.176840
BFGS:   13 21:48:01      -40.723173         0.176045
BFGS:   14 21:48:01      -40.725011         0.160965
BFGS:   15 21:48:01      -40.728039         0.115319
BFGS:   16 21:48:01      -40.730455         0.063112
BFGS:   17 21:48:02      -40.731504         0.044016
BFGS:   18 21:48:02      -40.731731         0.047425
BFGS:   19 21:48:02      -40.731799         0.044469
BFGS:   20 21:48:02      -40.731875         0.039502
BFGS:   21 21:48:02      -40.732018         0.030054
BFGS:   22 21:48:02      -40.732239         0.020031
BFGS:   23 21:48:02      -40.732459         0.013550
BFGS:   24 21:48:02      -40.732558         0.005217
BFGS:   25 21:48:03      -40.732574         0.001065
BFGS:   26 21:48:03      -40.732575         0.000161
BFGS:   27 21:48:03      -40.732575         0.000040
BFGS:   28 21:48:03      -40.732575         0.000008
BFGS:   29 21:48:03      -40.732575         0.000001
BFGS:   30 21:48:03      -40.732575         0.000000
BFGS:   31 21:48:03      -40.732575         0.000000
Minimization converged after 31 steps.
Maximum force component: 3.038126437542653e-09 eV/Angstrom
Maximum stress component: 2.1305528505569562e-10 eV/Angstrom^3
==== Minimized structure obtained from ASE ====
symbols =  ['Ni', 'Ni', 'Ni', 'Ni', 'Ti', 'Ti', 'Ti', 'Ti']
basis =  [[0.00000000e+00 9.28197991e-01 2.50000000e-01]
 [0.00000000e+00 7.18020088e-02 7.50000000e-01]
 [5.00000000e-01 4.28197991e-01 2.50000000e-01]
 [5.00000000e-01 5.71802009e-01 7.50000000e-01]
 [1.08292704e-36 6.49674695e-01 2.50000000e-01]
 [7.92737097e-37 3.50325305e-01 7.50000000e-01]
 [5.00000000e-01 1.49674695e-01 2.50000000e-01]
 [5.00000000e-01 8.50325305e-01 7.50000000e-01]]
cellpar =  Cell([[3.14940541110985, -1.6292315768335308e-36, 0.0], [-2.5321100053569415e-36, 9.457521736616552, 0.0], [0.0, 0.0, 3.7602724431936534]])
forces =  [[ 2.42621368e-33 -3.03812644e-09  3.70791490e-31]
 [-2.42621368e-33  3.03812644e-09 -3.70791490e-31]
 [ 3.03276709e-33 -3.03812644e-09  1.85395745e-31]
 [-3.63932051e-33  3.03812644e-09 -1.85395745e-31]
 [ 4.19641518e-46 -1.56737613e-09  1.85395745e-31]
 [-4.19641518e-46  1.56737613e-09 -1.85395745e-31]
 [ 9.09830128e-34 -1.56737613e-09 -1.85395745e-31]
 [-4.19641518e-46  1.56737613e-09  1.85395745e-31]]
stress =  [-1.26947422e-10 -2.13055285e-10 -2.05982885e-10  0.00000000e+00
  0.00000000e+00 -2.06911461e-34]
energy per atom =  -5.091571838296079
===============================================
Parameter sets [0] relaxed to duplicate structures, attempting to write only one of them.
Successfully added property instance for parameter set 0