element(s):
['Si']
AFLOW prototype label:
A_cI16_206_c
Parameter names:
['a', 'x1']
model type (only 'standard' supported at this time):
standard
number of parameter sets:
1
Parameter values for parameter set 0:
['6.657', '0.10135586']
model name:
MEAM_LAMMPS_JelinekGrohHorstemeyer_2012_AlSiMgCuFe__MO_262519520678_001
==== Building ASE atoms object with: ====
representative atom symbols =  ['Si']
representative atom coordinates =  [[0.10135586 0.10135586 0.10135586]]
spacegroup =  206
cell =  [[6.657, 0, 0], [0, 6.657, 0], [0, 0, 6.657]]
=========================================
      Step     Time          Energy          fmax
BFGS:    0 15:51:51      -69.961205         0.778606
BFGS:    1 15:51:51      -70.065593         0.575558
BFGS:    2 15:51:51      -70.095343         0.518120
BFGS:    3 15:51:51      -70.118626         0.454016
BFGS:    4 15:51:52      -70.162618         0.330563
BFGS:    5 15:51:52      -70.200562         0.347846
BFGS:    6 15:51:52      -70.233862         0.268900
BFGS:    7 15:51:52      -70.253205         0.085379
BFGS:    8 15:51:52      -70.254711         0.017800
BFGS:    9 15:51:52      -70.254865         0.002185
BFGS:   10 15:51:52      -70.254868         0.000249
BFGS:   11 15:51:52      -70.254868         0.000008
BFGS:   12 15:51:52      -70.254868         0.000000
BFGS:   13 15:51:52      -70.254868         0.000000
Minimization converged after 13 steps.
Maximum force component: 4.0412848463945606e-11 eV/Angstrom
Maximum stress component: 2.2670422218415502e-11 eV/Angstrom^3
==== Minimized structure obtained from ASE ====
symbols =  ['Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si', 'Si']
basis =  [[0.10244029 0.10244029 0.10244029]
 [0.39755971 0.89755971 0.60244029]
 [0.89755971 0.60244029 0.39755971]
 [0.60244029 0.39755971 0.89755971]
 [0.60244029 0.60244029 0.60244029]
 [0.89755971 0.39755971 0.10244029]
 [0.39755971 0.10244029 0.89755971]
 [0.10244029 0.89755971 0.39755971]
 [0.89755971 0.89755971 0.89755971]
 [0.60244029 0.10244029 0.39755971]
 [0.10244029 0.39755971 0.60244029]
 [0.39755971 0.60244029 0.10244029]
 [0.39755971 0.39755971 0.39755971]
 [0.10244029 0.60244029 0.89755971]
 [0.60244029 0.89755971 0.10244029]
 [0.89755971 0.10244029 0.60244029]]
cellpar =  Cell([[6.753209552269797, -5.917528446637178e-38, 0.0], [-4.225451672021987e-39, 6.753209552269797, 0.0], [0.0, 0.0, 6.753209552269797]])
forces =  [[-4.04128485e-11 -4.04128485e-11 -4.04128485e-11]
 [ 4.04128485e-11  4.04128485e-11 -4.04128485e-11]
 [ 4.04128485e-11 -4.04128485e-11  4.04128485e-11]
 [-4.04128485e-11  4.04128485e-11  4.04128485e-11]
 [-4.04128485e-11 -4.04128485e-11 -4.04128485e-11]
 [ 4.04128485e-11  4.04128485e-11 -4.04128485e-11]
 [ 4.04128485e-11 -4.04128485e-11  4.04128485e-11]
 [-4.04128485e-11  4.04128485e-11  4.04128485e-11]
 [ 4.04128485e-11  4.04128485e-11  4.04128485e-11]
 [-4.04128485e-11 -4.04128485e-11  4.04128485e-11]
 [-4.04128485e-11  4.04128485e-11 -4.04128485e-11]
 [ 4.04128485e-11 -4.04128485e-11 -4.04128485e-11]
 [ 4.04128485e-11  4.04128485e-11  4.04128485e-11]
 [-4.04128485e-11 -4.04128485e-11  4.04128485e-11]
 [-4.04128485e-11  4.04128485e-11 -4.04128485e-11]
 [ 4.04128485e-11 -4.04128485e-11 -4.04128485e-11]]
stress =  [-2.26704222e-11 -2.26704222e-11 -2.26704222e-11  0.00000000e+00
  0.00000000e+00 -3.15316572e-34]
energy per atom =  -4.390929268958306
===============================================
Parameter sets [0] relaxed to duplicate structures, attempting to write only one of them.
Successfully added property instance for parameter set 0