element(s):
['V']
AFLOW prototype label:
A_cF4_225_a
Parameter names:
['a']
model type (only 'standard' supported at this time):
standard
number of parameter sets:
1
Parameter values for parameter set 0:
['3.8599']
model name:
MEAM_LAMMPS_ShimKoKim_2013_AlVH__MO_344724145339_002
==== Building ASE atoms object with: ====
representative atom symbols =  ['V']
representative atom coordinates =  [[0 0 0]]
spacegroup =  225
cell =  [[3.8599, 0, 0], [0, 3.8599, 0], [0, 0, 3.8599]]
=========================================
      Step     Time          Energy          fmax
BFGS:    0 15:21:02      -20.877321         0.325806
BFGS:    1 15:21:02      -20.881566         0.282164
BFGS:    2 15:21:02      -20.893912         0.012208
BFGS:    3 15:21:02      -20.893934         0.000429
BFGS:    4 15:21:02      -20.893934         0.000001
BFGS:    5 15:21:02      -20.893934         0.000000
Minimization converged after 5 steps.
Maximum force component: 0.0 eV/Angstrom
Maximum stress component: 2.2234618324042517e-12 eV/Angstrom^3
==== Minimized structure obtained from ASE ====
symbols =  ['V', 'V', 'V', 'V']
basis =  [[0.00000000e+00 0.00000000e+00 0.00000000e+00]
 [0.00000000e+00 5.00000000e-01 5.00000000e-01]
 [5.00000000e-01 3.14486091e-36 5.00000000e-01]
 [5.00000000e-01 5.00000000e-01 6.28972182e-36]]
cellpar =  Cell([[3.8275340318073026, 4.710025866724664e-33, 3.544991979082084e-34], [5.2387892965819116e-33, 3.8275340318073026, -1.7573715581598713e-19], [-8.397406267406202e-35, -1.7573715581598764e-19, 3.8275340318073026]])
forces =  [[0. 0. 0.]
 [0. 0. 0.]
 [0. 0. 0.]
 [0. 0. 0.]]
stress =  [-2.22346183e-12 -2.22346183e-12 -2.22346183e-12  8.79746209e-30
 -2.62925289e-35  3.63715447e-53]
energy per atom =  -5.223483552719193
===============================================
Parameter sets [0] relaxed to duplicate structures, attempting to write only one of them.
Successfully added property instance for parameter set 0