element(s):
['Cu']
AFLOW prototype label:
A_cI2_229_a
Parameter names:
['a']
model type (only 'standard' supported at this time):
standard
number of parameter sets:
1
Parameter values for parameter set 0:
['2.8755']
model name:
EAM_Dynamo_MendelevKramerOtt_2009_CuZr__MO_600021860456_005
==== Building ASE atoms object with: ====
representative atom symbols =  ['Cu']
representative atom coordinates =  [[0 0 0]]
spacegroup =  229
cell =  [[2.8755, 0, 0], [0, 2.8755, 0], [0, 0, 2.8755]]
=========================================
      Step     Time          Energy         fmax
BFGS:    0 17:49:24       -6.481728        0.1715
BFGS:    1 17:49:24       -6.482896        0.1458
BFGS:    2 17:49:24       -6.485218        0.0472
BFGS:    3 17:49:24       -6.485421        0.0068
BFGS:    4 17:49:24       -6.485425        0.0002
BFGS:    5 17:49:24       -6.485425        0.0000
BFGS:    6 17:49:24       -6.485425        0.0000
Minimization converged after 6 steps.
Maximum force component: 0.0 eV/Angstrom
Maximum stress component: 1.744158104997469e-11 eV/Angstrom^3
==== Minimized structure obtained from ASE ====
symbols =  ['Cu', 'Cu']
basis =  [[0.  0.  0. ]
 [0.5 0.5 0.5]]
cellpar =  Cell([[2.8947490940504945, -2.92474314807668e-33, 1.013879165169802e-34], [-2.142329680248031e-33, 2.894749094050495, 1.0310088082246121e-19], [-4.385198671095769e-36, 1.0310088082246245e-19, 2.8947490940504945]])
forces =  [[0. 0. 0.]
 [0. 0. 0.]]
stress =  [1.74415810e-11 1.74415810e-11 1.74415810e-11 2.08188534e-28
 1.53224204e-35 1.34726319e-52]
energy per atom =  -3.242712602546519
===============================================
Parameter sets [0] relaxed to duplicate structures, attempting to write only one of them.
Successfully added property instance for parameter set 0