element(s):
['Si']
AFLOW prototype label:
A_cF4_225_a
Parameter names:
['a']
model type (only 'standard' supported at this time):
standard
number of parameter sets:
1
Parameter values for parameter set 0:
['3.868']
model name:
MEAM_LAMMPS_CuiGaoCui_2012_LiSi__MO_557492625287_002
==== Building ASE atoms object with: ====
representative atom symbols =  ['Si']
representative atom coordinates =  [[0 0 0]]
spacegroup =  225
cell =  [[3.868, 0, 0], [0, 3.868, 0], [0, 0, 3.868]]
=========================================
      Step     Time          Energy          fmax
BFGS:    0 15:38:47      -16.150577         0.990690
BFGS:    1 15:38:47      -16.188909         0.816147
BFGS:    2 15:38:47      -16.268153         0.254206
BFGS:    3 15:38:47      -16.277577         0.026123
BFGS:    4 15:38:47      -16.277682         0.000977
BFGS:    5 15:38:47      -16.277682         0.000004
BFGS:    6 15:38:47      -16.277682         0.000000
Minimization converged after 6 steps.
Maximum force component: 0.0 eV/Angstrom
Maximum stress component: 4.0108619073882365e-11 eV/Angstrom^3
==== Minimized structure obtained from ASE ====
symbols =  ['Si', 'Si', 'Si', 'Si']
basis =  [[0.00000000e+00 0.00000000e+00 0.00000000e+00]
 [1.29768479e-49 5.00000000e-01 5.00000000e-01]
 [5.00000000e-01 0.00000000e+00 5.00000000e-01]
 [5.00000000e-01 5.00000000e-01 0.00000000e+00]]
cellpar =  Cell([[3.9545105827876026, -2.8017152488541617e-33, 1.2378581107031166e-33], [-2.2114017466343585e-33, 3.9545105827876026, 5.437713221325101e-19], [-1.7403457289768626e-33, 5.437713221325137e-19, 3.9545105827876026]])
forces =  [[0. 0. 0.]
 [0. 0. 0.]
 [0. 0. 0.]
 [0. 0. 0.]]
stress =  [-4.01086191e-11 -4.01086191e-11 -4.01086191e-11  8.55367953e-28
 -7.37106930e-34  2.87160511e-50]
energy per atom =  -4.069420490093625
===============================================
Parameter sets [0] relaxed to duplicate structures, attempting to write only one of them.
Successfully added property instance for parameter set 0