element(s):
['Ni']
AFLOW prototype label:
A_cI2_229_a
Parameter names:
['a']
model type (only 'standard' supported at this time):
standard
number of parameter sets:
1
Parameter values for parameter set 0:
['2.7844']
model name:
EAM_Dynamo_FoilesBaskesDaw_1986Universal3_Ni__MO_580571659842_000
==== Building ASE atoms object with: ====
representative atom symbols =  ['Ni']
representative atom coordinates =  [[0 0 0]]
spacegroup =  229
cell =  [[2.7844, 0, 0], [0, 2.7844, 0], [0, 0, 2.7844]]
=========================================
      Step     Time          Energy          fmax
BFGS:    0 16:18:37       -8.800685         0.192433
BFGS:    1 16:18:37       -8.802058         0.140606
BFGS:    2 16:18:37       -8.803660         0.003376
BFGS:    3 16:18:37       -8.803661         0.000062
BFGS:    4 16:18:37       -8.803661         0.000000
BFGS:    5 16:18:37       -8.803661         0.000000
Minimization converged after 5 steps.
Maximum force component: 0.0 eV/Angstrom
Maximum stress component: 2.083859068305829e-14 eV/Angstrom^3
==== Minimized structure obtained from ASE ====
symbols =  ['Ni', 'Ni']
basis =  [[0.  0.  0. ]
 [0.5 0.5 0.5]]
cellpar =  Cell([[2.798870797095705, -3.482473191638561e-33, -2.4633909962226546e-36], [-2.477737034529586e-33, 2.798870797095705, 4.989340928560045e-21], [-4.468642177542235e-34, 4.989340928561425e-21, 2.798870797095705]])
forces =  [[0. 0. 0.]
 [0. 0. 0.]]
stress =  [-2.08385907e-14 -2.08385907e-14 -2.08385907e-14 -9.81326842e-32
  4.91705176e-35  1.37801107e-51]
energy per atom =  -4.401830441032552
===============================================
Parameter sets [0] relaxed to duplicate structures, attempting to write only one of them.
Successfully added property instance for parameter set 0