element(s):
['Cu']
AFLOW prototype label:
A_cF4_225_a
Parameter names:
['a']
model type (only 'standard' supported at this time):
standard
number of parameter sets:
1
Parameter values for parameter set 0:
['3.6146']
model name:
MEAM_LAMMPS_WangOhLee_2020_CuMo__MO_380272712420_002
==== Building ASE atoms object with: ====
representative atom symbols =  ['Cu']
representative atom coordinates =  [[0 0 0]]
spacegroup =  225
cell =  [[3.6146, 0, 0], [0, 3.6146, 0], [0, 0, 3.6146]]
=========================================
      Step     Time          Energy         fmax
BFGS:    0 16:55:57      -14.159976        0.0111
BFGS:    1 16:55:57      -14.159981        0.0099
BFGS:    2 16:55:57      -14.160000        0.0000
BFGS:    3 16:55:57      -14.160000        0.0000
BFGS:    4 16:55:57      -14.160000        0.0000
Minimization converged after 4 steps.
Maximum force component: 0.0 eV/Angstrom
Maximum stress component: 1.3018170900857792e-14 eV/Angstrom^3
==== Minimized structure obtained from ASE ====
symbols =  ['Cu', 'Cu', 'Cu', 'Cu']
basis =  [[0.00000000e+00 0.00000000e+00 0.00000000e+00]
 [4.73407132e-50 5.00000000e-01 5.00000000e-01]
 [5.00000000e-01 0.00000000e+00 5.00000000e-01]
 [5.00000000e-01 5.00000000e-01 0.00000000e+00]]
cellpar =  Cell([[3.613315683979628, 1.244138779533758e-33, 4.453880861240897e-33], [1.5641522517871305e-33, 3.613315683979628, 5.2258713751676737e-23], [-3.289846794413809e-33, 5.2258713759068087e-23, 3.613315683979628]])
forces =  [[0. 0. 0.]
 [0. 0. 0.]
 [0. 0. 0.]
 [0. 0. 0.]]
stress =  [ 1.30181709e-14  1.30181709e-14  1.30181709e-14 -2.13353673e-30
 -3.54029878e-34  2.53271830e-50]
energy per atom =  -3.5400000001356364
===============================================
Parameter sets [0] relaxed to duplicate structures, attempting to write only one of them.
Successfully added property instance for parameter set 0