This potential was developed to accurately reproduce properties of a single phase of the Ni-Al system, namely, B2-NiAl. Properties of other phases of this system are reproduced less accurately. Application of this particular potential to simulations of pure Ni or pure Al is not recommended.

The paper reporting on this potential (G.P. Purja Pun and Y. Mishin, "Development of an interatomic potential for the Ni-Al system," Phil. Mag. 89, 3245 (2009)) contains an error in Table 6. The generalized stacking fault energies in Ni3Al listed in this table are incorrect. The correct energies computed with the new potential are (in J/m2): APB (111) 180 CSF (111) 229 SISF (111) 21 APB (100) 20

This model was developed as a prototype case for the Gibbs-Duhem protocol for optimizing melting points. As such, the melting point was the primary metric for its development. We have shown that the modifications to the original Mei-Davenport potential that we used to optimize T_m did not change the quality of the potential with respect to elastic constants, density, etc., but no systematic study of other properties was performed.

Model was fit to room temperature properties and extrapolated, classical (i.e. non-quantum) low temperature properties. The intended application is for shock compression simulations, but validation against shock pressure conditions is limited. The model appears to provide accurate results in the elastic shock regime (i.e. pressure ~ 5 to 10 GPa), as documented in the paper by Zimmerman, Winey and Gupta (Phys. Rev. B, 2011). Behavior at higher pressures and in the elastic-plastic regime is unknown.

This model was automatically fit using Lorentz-Berthelot mixing rules. It reproduces the dimer equilibrium separation (covalent radii) and the bond dissociation energies. It has not been fitted to other physical properties and its ability to model structures other than dimers is unknown.